纯度高, 高分子量,刚性高, 高 ESCR（抗应力开裂）, 食品接触的合规性, 果汁瓶, 瓶子, 护罩, 食品包装, 外壳, 吹塑成型, 注射成型

 

SABIC® HDPE B6246LS

高密度聚乙烯

Saudi Basic Industries Corporation (SABIC)

Technical Data

 

产品说明

SABIC® HDPE B6246LS is SABIC's latest high density polyethylene development for the food and beverage industry. This grade meets the latest end consumer expectations regarding purity, healthiness and organoleptics. These "green" market trends resulted in the launch of this unique SABIC grade, suited for state of the art blow moulding as well as injection moulding applications. It combines a high rigidity with superb processing performance, which offers potential for system cost reduction.

 

The grade is very suited for the blow moulding of mono as well as multi layer bottles in several food markets, like fresh, pasteurised and ultra heat treated milk, sauces, orange juice, functional drinks, probiotics and other "daily shot" drinks. The unique properties offer the possibility to reduce weight at very good top load strength. This slip agent free grade is also very suited for the injection moulding of caps & closures for carbonated soft drinks and sparkling water.

 

The material can also be used for injection moulding applications requiring a very high environmental stress cracking resistance, like UN-pails and UN-caps & closures.

 

In contrast to the standard SABIC® HDPE injection moulding port folio, this grade is produced with a Cr catalyst.

 

The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet (English)

•  Technical Datasheet (English)

搜索 UL 黄卡 •  Saudi Basic Industries Corporation (SABIC)

供货地区 • 欧洲

• 纯度高 • 高分子量 • 良好的感官特征

特性 • 刚性，高 • 高强度

• 食品接触的合规性

• 高 ESCR（抗应力开裂） • 可加工性，良好

用途 • 果汁瓶 • 瓶子 • 外壳

• 护罩 • 食品包装

形式 • 粒子

加工方法 • 吹塑成型 • 注射成型

 

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 0.962g/cm³ 0.962g/cm³ ISO 1183

熔流率（熔体流动速率） ISO 1133

190°C/2.16 kg 0.50g/10 min 0.50g/10 min

190°C/21.6 kg 46g/10 min 46g/10 min

190°C/5.0 kg 2.5g/10 min 2.5g/10 min

抗环境应力开裂 3 内部方法

167°F (75°C), 0.0394 in (1.00 mm), 5.00hr 5.00hr

Rhodacal-DS10

机械性能 额定值(英制) 额定值(公制) 测试方法

拉伸模量 ISO 527-2/1BA/50

73°F (23°C), 0.0787 in (2.00 mm), 模压成型 189000psi 1300MPa

拉伸应力 ISO 527-2/1BA/50

屈服, 73°F (23°C), 0.0787 in (2.00 mm), 4210psi 29.0MPa

模压成型

断裂, 73°F (23°C), 0.0787 in (2.00 mm), 2610psi 18.0MPa

模压成型

拉伸应变 ISO 527-2/1BA/50

断裂, 73°F (23°C), 0.0787 in (2.00 mm), > 1000% > 1000%

模压成型

弯曲模量 ISO 178

73°F (23°C), 0.0787 in (2.00 mm), 模压成型 232000psi 1600MPa

 

SABIC® HDPE B6246LS

高密度聚乙烯

Saudi Basic Industries Corporation (SABIC)

机械性能 额定值(英制) 额定值(公制) 测试方法

弯曲应力 ISO 178

73°F (23°C), 0.0787 in (2.00 mm), 模压成型 4500psi 31.0MPa

冲击性能 额定值(英制) 额定值(公制) 测试方法

悬壁梁缺口冲击强度 ISO 180/A

-22°F (-30°C), 模压成型 3.3ft•lb/in² 7.0kJ/m²

73°F (23°C), 模压成型 6.2ft•lb/in² 13kJ/m²

硬度 额定值(英制) 额定值(公制) 测试方法

肖氏硬度 (邵氏 D, 73°F (23°C), 模压成型) 64 64 ISO 868

热性能 额定值(英制) 额定值(公制) 测试方法

热变形温度 (66 psi (0.45 MPa), 未退火) 192°F 89.0°C ISO 75-2/B

维卡软化温度 264°F 129°C ISO 306/A

溶融温度（DSC） 275°F 135°C ISO 11357-3

Enthalpy Change 225J/g 225J/g ISO 11357-3

 

 

 

 

 

 

 

 

 